This method describes the procedures for compacting asphalt samples using the SGC and determining their percent compaction. This method consolidates the provisions of AASHTO T312 and makes the following exceptions:

·        Compaction temp



Standard Specification 2303 Flexible Pavement

AASHTO T312 Standard Method for Preparing and Determining the Density of Hot Mix Asphalt (HMA) Specimens by Means of the Superpave Gyratory Compactor

IM 321 Compacted Density of Asphalt Concrete

IM 357 Preparation of Bituminous Samples for Test




·        SGC, including a device for measuring and recording the height of the specimen throughout the compaction process. The compactor may also include a printer or a computer and software for collecting and printing the data.

·        Specimen molds per AASHTO T312

·        Thermometer with a range of 38 to 200°C (100 to 400°F).

·        Balance with a minimum capacity of 6,000 gram and readable to at least 1 gram.

·        Forced Draft Oven capable of maintaining a constant temperature of 177 ± 3°C (350 ± 5°F) and large enough to hold 2 molds and mix pans.

·        Pan between approximately 200 in.2 and 300 in.2 in size.

·        Safety equipment: insulated gloves, long sleeves, apron, etc.


General Equipment:


·        Calibration equipment recommended by compactor manufacturer

·        Paper discs with a diameter of 150 mm (6 in.).

·        Lubricating materials recommended by compactor manufacturer

·        Scoop or trowel for moving mixture

·        Funnel or other device for ease of loading mixture into mold.






The means of calibrating the gyratory vary with different manufacturers. Refer to the operation manual and manufacturer’s recommendations of the particular brand and model of gyratory available for use. Calibration of the following items should be verified at the noted intervals unless manufacturer’s recommendations are more stringent:







Calibration Interval


Record to nearest 0.1 mm,

Compact to 115 + 5 mm



Angle (Internal)


1.16° ± 0.02°


See IM 208




600 + 18 kPa


See IM 208


Speed of Rotation


30.0 + 0.5 gyrations per minute


See IM 208

Mold dimension

149.90 to 150.00 mm1

See IM 208

Platen dimension

149.50 to 149.75 mm

See IM 208

1.       Molds with inside diameters up to 150.20 mm, measured according to AASHTO T312 may be used.




1.     Turn the compactor on and allow for warm-up before proceeding.


2.     Lubricate the mold or gyratory parts as recommended by the manufacturer.


3.     Perform the height calibration per manufacturer’s recommendations.


4.     Set the specified number of gyrations, Ndes.




1.     Obtain the material for the test specimen by following the procedure in IM 357.


2.     Weigh into separate pans for each specimen the amount of asphalt mixture required which will result in a compacted specimen 115 ± 5 mm in height. Spread the material uniformly in the pan to between 1 to 2 in. of thickness.


This will normally be about 4700 grams.


3.     Heat the pans of loose asphalt mixture in the oven to a temperature of 135 ± 2°C (275 ± 5°F) as checked by a thermometer with the bulb in the center of the mixture sample. The oven temperature may not exceed 143°C (290°F).


Heat WMA mixtures to 240 ± 5°F.


a.     Heat the mold, base plate, top plate (if used) and funnel (if used) in the oven for each specimen compacted for a minimum of 30 minutes. In between tests, a minimum of 5 minutes reheating should be used.


4.     Place a paper disc in the bottom of the mold. Place the mixture into the mold in one lift. A funnel or other device may be used to place the mixture into the mold. Take care to avoid segregating the mix in the mold, but work quickly so that the mixture does not cool excessively during loading. Level the mix in the mold and place a paper disc on top.


5.     Place the mold in the gyratory.


6.     If the desired number of gyrations (Ndes ) has not been entered into the gyratory, do that now. The number of gyrations to apply is determined from the Job Mix Formula (JMF).


NOTE: Some gyratories allow charging the mold with mix after the mold has been positioned in the compactor.


7.     Apply the load to the mixture in the mold.


8.     Apply the gyratory angle to the specimen.


9.     Compact to Ndes.


10.  After compaction is complete, remove the angle from the specimen, and raise the loading ram if needed (this is done automatically on some gyratories).


11.  Extrude the specimen from the mold. Take care not to distort the specimen when removing the specimen from the mold. Remove the paper discs while the specimen is still warm to avoid excessive sticking.


12.  Record or print the height data for each specimen compacted.


NOTE: A cooling period of 5 to 10 minutes before extruding the specimen may be necessary with some mixtures; a fan may help speed the cooling process.


13.  After the specimens have cooled, they may be tested for bulk specific gravity, Gmb per IM 321.