INSPECTION & ACCEPTANCE

RAPID-SETTING CONCRETE PATCHING MATERIALS FOR PAVEMENTS

 

GENERAL

Acceptance of rapid-setting concrete patching materials will be on the basis of approved brands and satisfactory test results. These materials are approved for use when the plans and/or specifications permit their use for surface patching purposes.

 

Brand names must be identifiable on the packages. Material shall be packaged in a multi-wall moisture resistance paper bag. Shelf life shall be indicated on each packaged bag (by expiration date). Mixing sequence and addition of mixing water for each material shall be as directed and recommended by each manufacturer. When coarse aggregate is used, its type and quantity shall follow manufacturer recommendations and a minimum of Class 2 durability rating. Approved manufacturers and brands of rapid-setting concrete patching materials are listed in the Materials Approved Products Listing Enterprise (MAPLE) as Appendixes A and B for two types of applications.

 

APPROVAL

To obtain approval of a rapid-set concrete patching material, the manufacturer shall submit the following items to the Office of Construction and Materials in Ames:

 

1.   Product identification including brand name,

2.   Complete manufacturer's recommendation for usage,

3.   A copy of test report for the submitted product from the National Transportation Product Evaluation Program (NTPEP), and

4.   A current Materials Safety Data Sheet (MSDS).

 

Appendix A consists of rapid set patching materials for pavement patching. Appendix B consists of shrinkage compensated rapid set patching materials for dowel bar retrofit projects. Product approval is based on satisfactory evaluation of the NTPEP test report. The minimum requirements for approval are listed in the following table. When aggregate extension is allowed for a product, both neat and extended mixes shall meet the criteria listed in the table.

 

 

AASHTO/ASTM Test Method

 

Cure Time

 

Appendix A

 

Appendix B

Initial Set, minutes, minimum 

T131 or C403

 

12

12

Compressive Strength,

psi, minimum

T22 or T106

3 hours

24 hours

1,000

3,000

3,000

5,000

Bonding: Slant Shear or Direct Tension, psi, minimum

C882

C1583

1 day

28 days

1,000

300

1,000

300

Durability Factor,  minimum

T161 Method A or Method B

14-day moist cure

70%

(300 cycles)

90%

(300 cycles)

Length Change,

allowable

T160

28 days in water

28 days in air

+0.15%

-0.15%

+0.15%

-0.05%

Resistivity or

Rapid Chloride

Permeability, maximum

T358

T277

28-day moist cure

28-day moist cure

29 k-ohm-cm

1,500 coulombs

21 k-ohm-cm

1,000 coulombs

Acid-Soluble Chloride Content, maximum

C1152

 

 

0.08%

by weight

Magnesium phosphate-based patching materials will not be allowed on Appendixes A and B due to its poor freeze-thaw durability.

 

Manufacturer shall provide the acid-soluble chloride result from an independent test agency for review.

 

Approval of a product may be withdrawn at any time because of deficient test results, inadequate documentation, and/or lack of product identification.

 

CERTIFICATION

The manufacturer shall file a certification at the beginning of each calendar year stating that the material supplied during that year is identical with the formulation previously tested and approved by the Office of Construction and Materials.

 

MONITOR SAMPLING & TESTING

The Office of Construction and Materials may sample and test rapid-setting concrete patching materials to verify their capabilities of meeting the approval requirements.